Nanocompósitos de elastômero termoplástico à base de PP/EPDM/argila organofílica

Abstract

In this work it was prepared nanocomposites based in PP/EPDM thermoplastic elastomer and organoclay. Maleinized polypropylene and ethylene-propylene-diene rubber, PP-MA and EPDM-MA, respectively, were employed as interfacial agents. Also two kinds of organoclays, differing about surfactant chemical structure and as consequence thermal stability, were investigated as inorganic filler. Nanocomposites were prepared by melt intercalation in an internal chamber mix and organoclay was incorporated by masterbatches addition, which ones were previously made. It was investigated the influence of amount and kind of organoclay and interfacial agent on tensile properties, rheology and morphology (crystallinity and structure type) of nanocomposites obtained. The results showed that interfacial agents addition promoted a better dispersion degree of organoclay platelets in PP/EPDM matrix, mainly PP-MA. Nanocomposites with both intercalated and exfoliated structures were obtained. These exhibited higher Young modulus and kept their elongation values. The better dispersion degree of clay platelets in nanocomposites containing PP-MA was confirmed by rheology measurements. Increasing amounts of organoclay lowered the crystallinity degree of nanocomposites but the reprocessability was maintained similar to that of pure TPE. Finally, the chemical structure of surfactants did not change the intercalation/exfoliation process due to the similarity of organoclay basal spacing and moderated TPE processing temperature.